Veneziani Colloidal Silica 0,75 Lt #473COL314

Veneziani Colloidal Silica 0,75 Lt #473COL314

Veneziani Colloidal Silica 0,75 Lt #473COL314

MICROSILICE belongs to the range of additives to be mixed with RESINA 2000 in order to produce compounds with different properties.
Price:
€15.67
Listing:
€18.43
You Save:
€2.77 (15%)

Description

MORE INFORMATION

SUITABLE TO PRODUCE COMPOUNDS FOR:

GLUING OF ACCESSORIES

LAMINATIONS

JOINING


FEATURES
MICROSILICE belongs to the range of additives to be mixed with RESINA 2000 in order to produce compounds with different properties. MICROSILICE is a thickening additive used with RESINA 2000. Best suited for gluing, jointing and the repair of defective spots. It may be mixed together with other additives of the range in order to improve knife application and appearance of the product and is suitable for both above and below waterline applications.

TECHNICAL DATA
Curing mechanism:                /
Specific weight: 1.00 ± 0.02 kg/lt
Volume solids:                        /
Flash point:                            /
Appearance:                          /
Color:                                white
Unit size:                         0,75 lt

SURFACE PREPARATION
Before applying Resina 2000, the surface must be completely dry and clean. Wooden surfaces must be dry and clean, as well as free from grease and oil. The areas to be treated should be sandpapered at first.

APPLICATION
MICROSILICE to be added to RESINA 2000 only after component A has been mixed thoroughly with component B with a ratio of 2:1.

Gluing and laminating: Mix 2 parts of already catalysed Resina 2000 +1 part of Microsilice, in order to produce a liquid compound suitable for gluing of small parts and laminations.

Jointing, filling, gluing of accessories : Mix 1 part of already catalysed Resina 2000 + 1 part of Microsilice, in order to produce a paste suitable for jointing, gluing of accessories and as an all purpose filler.

Extensive filling and jointing: Mix 1 part of already catalysed Resina 2000 + 2 parts of Microsilice, in order to produce a structural compound suitable for extensive jointing and filler application.

APPLICATION DATA
Drying time before use (20 ° C):     /
Pot life (20 ° C):                             /
Application temperature min / max: + 5 / + 25 ° C
Hardener:                                      /
Mixing ratio by volume:                 /
Mixing ratio by weight:                  /
Thinner:                                         /
Wet film thickness per coat:          /
Dry film thickness per coat:           /
Theoretical coverage:                   /
Recoating time at 20 ° C min / max /
Number of coats:                          /