MICROFIBRE belongs to the range of additives to be mixed with RESINA 2000 in order to produce compounds with different properties
Price:
€42.75
Listing:
€50.29
You Save:
€7.54 (15%)

Description

Unit size 2.5 lt.
White colour.

MORE INFORMATION

MICROSPHERES
HOLLOW GLASS MICROSPHERES
SUITABLE FOR OBTAINING FOLLOWING COMPOUNDS:
SELF-LEVELLING
FILLING COMPOUNG
FILLERS

FEATURES
MICROSFERE belongs to the range of additives to be mixed with RESINA 2000 in order to produce compounds with different properties. MICROSFERE consists of microspheres with low moisture absorption and can therefore used for applications above and below the waterline. Their main purpose is the production of fillers with low specific gravity, which are easy to sand and with a variable consistency according to the needs of the user. These fillers are best suited for the repair of horizontal cracks, small surface defects and as knifing fillers.

TECHNICAL DATA
Curing mechanism:      /
Specific weight:           /
Volume solid: 100 %    /
Flash point:                 / 
Appearance:                /
Colour:                   WHITE
Unit sizes:     0,75 L/ 2,50 litres

SURFACE PREPARATION
Before applying Resina 2000, the surface must be completely dry and clean. Wooden surfaces must be dry and clean, as well as free from grease and oil. The areas to be treated should be sandpapered first.

APPLICATION
MICROSFERE to be added to RESINA 2000 only after component A has been mixed thoroughly with component B with a ratio of 2:1.

Liquid compound: Mix 2 parts of already catalysed Resina 2000 + 1 part of Microsfere, in order to produce a liquid compound suitable for the repair of horizontal cracks and for gluing.

Filling compound: Mix 1 part of already catalysed Resina 2000 + 1 part of Microsfere, in order to produce a half-liquid, self-levelling compound suitable as a filling compound for small surface defects and as a knifing filler.

Filler: Mix 1 part of already catalysed Resina 2000 + 3 parts of Microsfere, in order to produce a filler suitable to be applied at high thickness.

APPLICATION DATA
Drying time before use (20°C): /
Pot life (20°C):                        /
Application temperature min/max: +5/+25 °C
Hardener:                               /
Mixing ratio by volume:           /
Mixing ratio by weight:            /
Thinner:                                  /
Wet film thickness per coat:     /
Dry film thickness per coat:      /
Minimum covering time  (20°C)
Maximum covering time (20°C)
Number of coats:                     /