HEMPEL HIGH PROTECT is a two-component high build amine adduct epoxy primer, solvent-free. It forms a hard, tough and water-resistant coating.
Price:
€148.23
Listing:
€197.64
You Save:
€49.41 (25%)

Description

MORE INFORMATION

Unit size 2.5Lt. Cream.

HIGH PROTECT A + B PRIMER

PHYSICAL CONSTANTS:
Finish: High gloss
Volume solids,% 100
Theoretical coverage: 2.9 m2 / l [116.3 sq.ft. / US gallon] - 350 micron / 14 mils
Flash point: 74 ° C [165.2 ° F]
Specific weight: 1.3 kg / liter [10.5 lb / US gallons]
Touch dry: 10-12 hour (s) 20°C / 68°F, 22 to 27 hours at 10°C / 50°F
Fully cured: 7 days (i) 20°C / 68°F, 14 days (i) at 10°C / 50 ° F
VOC content: 10 g / l [0.1 lb / US gallons]

APPLICATION DETAILS:
Mixing ratio: 3: 2 by volume
Application method: Airless / brush / sponge roller
Thinner, (volume max): Do not dilute
Pot life: 45 minutes (i) 20°C / 68°F, 60 minutes at 15°C / 59°F
Hole nozzle: 0.023 "
Nozzle pressure: 250 bar [3625 psi] (Airless spray data are indicative and subject to adjustment)
Cleaning equipment: HEMPEL'S THINNER 08451 The roller is discarded after use.
Dry thickness indicated 350 micron [14 mils]
Thick wet indicated 350 micron [14 mils]
Recoat interval, min to specification.
Recoat interval, max As per specification.

SURFACE PREPARATION:
Wash the area to be treated with HEMPEL'S PRE-CLEAN 67602 as set out in the instructions and rinse with fresh water. Remove salt and other contaminants by cleaning with fresh water at high pressure.
Fibreglass: The surface should be abraded with to uniform roughness (sandpaper, grit 80-100). Remove any dust.
Steel: Sand to Sa 2½, ISO 8501-1: 2007, surface profile corresponding to Rugotest No. 3, BN 11.

PRODUCT APPLICATION:
Use only where application and curing take place at temperatures higher than 10°C / 50°F. The temperature of the paint must be equal to 15°C or higher. When applying, the surface must be perfectly clean, dry and temperature must be above the dew point to prevent the formation of condensation.
Fibreglass: For osmosis repairs, apply at least 2 layers with dry film thickness of 350 microns each (at least 4 layers with dry film thickness of 150 microns each for roller applications). For preventive treatments, apply at least one layer with a dry film thickness of 350 microns each (at least 2 layers with dry film thickness of 150 microns each for roller applications).
Steel: minimum 3 layers of 150 micron / 6 mils dry film thickness each.

Application equipment
We recommend using ½ '' hoses between the pump and the spray gun to avoid pressure drops and, if possible, remove the suction hose.

Film thickness / dilution
A different thickness may be specified, depending on use and area of ​​use. This will alter coverage. For roller application, it is essential to ensure that the layer of the specified film is not porous.

Catalyst
The catalyst is highly thixotropic. Add 3 basic parts to 2 parts of catalyst during stirring.

Undocking
The boat should not be put back in the water prior to one week from catalysis of the last layer of the product (20°C). 2 weeks at 10°C / 50°F.

Overcoating
If the interval is exceeded, it will be necessary to apply a thin coat of HEMPEL'S LIGHT PRIMER 45551. After prolonged exposure to the elements, before recoating completely clean the surface using high-pressure cleaning with fresh water and allow to dry.