Veneziani Microfibre 2.5Lt White #473COL285

Veneziani Microfibre 2.5Lt White #473COL285

Veneziani Microfibre 2.5Lt White #473COL285

MICROFIBRE belongs to the range of additives to be mixed with RESINA 2000 in order to produce compounds with different properties
Price:
€42.75
Listing:
€50.29
You Save:
€7.54 (15%)

Description

MORE INFORMATION

FEATURES:
Microfibre belongs to the range of additives to be mixed with RESINA 2000 (our code COL226, COL227) to produce compounds with different properties. Microfibre consists of microfibres with an average length of 500 microns which, when mixed with RESINA 2000 (our codes COL226, COL227), create a strong compound, owing to a multidirectional internal structure. Due to the low absorbency of resin, the penetration capacity of Resina 2000 is not affected. The main purpose is the gluing of T-joints, where a filler with high viscosity and high mechanical resistance is required. Ieal for filling horizontal cracks, small surface imperfections, etc.

TECHNICAL DATA:
Curing Mechanism: /
Specific weight: /
Volume solids: 100 %
Flash point: /
Film appearance: /
Colour: White
Unit size: 2,50 L

SURFACE PREPARATION
Before intervening with Resina 2000, make sure that the surface to be treated is completely dry. The wood to be treated must be clean, dry and  free of oil and/or diesel, etc. Sand the surfaces prior to application.


APPLICATION PROCEDURE
Add the additive to RESINA 2000 only after carefully mixing component A and component B in a 2:1 ratio.
Fluid glue: Mix 2 parts of catalyzed RESINA 2000 + 1 part of Microfibre to obtain a fluid glue suitable for gluing surfaces with small imperfections
Structural bonding: Mix 1 part of catalyzed RESINA 2000 + 1 part of Microfibre to obtain a light structural compound suitable for bonding surfaces with large imperfections.
High-density structural bonding: Mix 1 part of catalyzed Resin 2000 + 2 parts of Microfibre to obtain a high-density structural compound capable of remaining in position even in vertical applications.

Unit size 2.5lt. White.